The Effect of Crystallization of SLS Glass for Bulletproof Materials
Gyu-In Shim, Tae-Yoon Kim, Se-Young Choi
Yonsei University
방탄소재 활용을 위한 SLS 유리 결정화의 효과
심규인, 김태윤, 최세영
연세대학교
Abstract
For application of transparent bulletproof materials, the SLS(soda-lime-silicate) glass was heated by 2-step crystallization. The DTA curve for SLS glass revealed the nucleation and crystal growth temperature at about $575^{circ}C$ and $675^{circ}C$, respectively. The crystallized glass was heated at various conditions(temperature, time). As a result, the maximum nucleation and crystal growth rates were $3.8 imes10^5/mm^3{cdot}hr$ at $575^{circ}C$ and 20.58nm/min at $680^{circ}C$, respectively. The bending strength, fracture toughness and vickers hardness were 451.7MPa, $0.9388MPa{cdot}m^{1/2}$, and $693.9H_v$ which were 201%, 31%, and 22% higher than parent glass, respectively. Surface image and transmittance of crystallized SLS glass were analyzed by optical microscopy and UV/VIS/NIR spectrophotometer. Transmittance of crystallized SLS glass at visible-range(200~800nm) was not changed.
Key Words: SLS Glass Crystallization Bulletproof Nucleation, Crystal Growth


ABOUT
ARTICLE CATEGORY

Browse all articles >

BROWSE ARTICLES
FOR CONTRIBUTORS
Editorial Office
160 Bugyuseong-daero 488beon-gil, Yuseong-gu, Daejeon 34060, Korea
Tel: +82-42-823-4603    Fax: +82-42-823-4605    E-mail: kimst@kimst.or.kr                

Copyright © 2024 by The Korea Institute of Military Science and Technology.

Developed in M2PI

Close layer
prev next